The deformation dislocation density and martensite microstructure were also analysed by TEM .

采用 TEM对形变位错密度以及马氏体组织进行了分析。

The micro-holes in alumite film anodized in oxalic acid are investigated by transmission electron microscopy ( TEM ) .

采用透射电镜（ TEM）观察了草酸溶液中形成的铝阳极氧化膜中纳米级微孔的形貌。

Partition ratio of alloy element in two phase and misfit degree were measured and analyzed by TEM with EDS.

利用 透射 电镜的EDS对合金元素在两相中的分配比和错配度进行测试和分析。

The dynamic recrystallization mechanism during hot compress was examined by the true stress-strain curves and TEM .

采用真应力一真应变曲线和 TEM研究其高温压缩变形中的流变应力行为和它的动态再结晶过程。

The systematic tilting method is an important operation technique of transmission electron microscope ( TEM ) .

系统倾转样品是 透射电子显微镜操作的一种重要 实验技术。

One-dimension carbon nanomaterials with variant morphologies from ethanol flames were studied systematically by using scanning electron microscopy ( SEM ) and transmission electron microscopy ( TEM ) .

文章利用扫描电镜（SEM）、透射电镜（ TEM）系统观察和研究了乙醇燃烧火焰中合成的具有各种不同形貌特征的一维碳纳米材料。

The study showed that PB-gPS latex particle is ball-like and has a core-shell shaped structure .

利用 TEM 对 PB-g-PS乳胶粒子 进行了 形态 观察， 接枝 物为球形粒子，且具有核壳结构。

The sample has to be this thin for the TEM to work .

样品必须达到这么薄，才能适合 TEM工作。

Abstract : The microstructure of forged white cast iron was observed and investigated by means of SEM and TEM .

文摘：借助扫描电镜、 透射电镜观察和分析了白口铸铁的微观组织。

The microstructure was observed by OM and TEM and the composition was analyzed by EDS method .

利用OM、 TEM和EDS技术对钢球内部的显微组织和成分进行观察和分析；

In detail the microstructures shown by TEM for the nano-and ultranano-crystalline diamond can also be observed in ballas diamond .

TEM显示的纳米和超纳米晶金刚石显微结构在半刚石中也能看到。

The coating structure is characterized by direct image of TEM and indirect analysis of component .

包覆结构主要用 透射 电镜直接观测和成分对比分析等间接手段表征。

The GNFs have been characterized by UV-visible spectroscopy transmission electron microscopy ( TEM ) X-ray diffraction ( XRD ) and electrochemical measurements .

我们已经通过可见紫外光谱、 透射电子显微术、X射线衍射和电气化学测量法对金纳米花的特性进行了分析。

The density change and mechanical properties during the rolling process at ambient temperature were examined and its microstructure was observed by SEM and TEM .

探索了板材轧制过程中材料的密度变化规律及室温力学性能，通过金相、扫描电镜和 透射电镜观察了其微观组织。

The particles were observed by TEM and the selected area electron diffraction patterns of nickel powders were shown ;

运用 TEM 技术观察了两种粉体的形貌，并给出了选区电子衍射图；

SEM and TEM results showed that CNTs dispersed homogeneously in the compound powder and combined firmly with superfine Cu .

SEM和 TEM结果表明，碳纳米管均匀地分散在超细铜粉中，并且与铜颗粒形成较牢固的结合。

In this paper remaining austenite in G50 steel was determined and its appearance was observed by TEM .

本文叙述了对G50钢中残余奥氏体的测定和由 透射电镜观察到的残余奥氏体形貌特征。

The solid state amorphization reactions induced by a constant-heating-rate annealing in themultilayers were studied by means of XRD SEM TEM DSC and magnetic analysis .

使用XRD，SEM， TEM，DSC和磁性分析方法研究了该多层由恒速升温退火导致的固态非晶化反应。

TEM observation showed that there was much stacking fault in nanowires .

TEM观察显示，纳米线中存在大量的堆垛层错缺陷。

TEM and SEM were used to test the structure and figure of polyamine flocculants .

利用 电子 透射 电镜和电子扫描电镜对聚合物的结构形貌进行了表徵。

The changes of Golgi apparatus during spermatogenesis of Macrobrachium nipponense were studied with transmission electron microscopy ( TEM ) .

用 透射电镜技术研究了日本沼虾精子发生过程中生精细胞内高尔基体的变化。

By means of optical microscope SEM with EPMA system X-ray diffraction TEM and microhardness tester the compositions structures and properties of the alloyed zone were determined .

用光学显微镜、扫描电镜、电子探针、x射线衍射、 透射 电镜、显微硬度计等手段分析了合金化区域的成分、组织和性能。

In this paper the effects of heat treatment on nano-size ITO powder during its preparation were studied with the characterization by TG-DTA TEM and XRD .

文章主要研究了水相共沉淀法制备ITO粉体过程中，热处理温度对粉体形成过程的影响，并用TG&DTA、 TEM和XRD对其作了表征分析。

The structure and ultrastructure of adult of Paragonimus heterotremus were observed by light microscope and transmission electron microscope ( TEM ) .

采用光镜和 透射电镜对异盘并殖吸虫成虫的结构和超微结构进行了观察。

The structure and morphology of the obtained carbon fibers are characterized by scanning electron microscopy ( SEM ) and transmission electron microscopy ( TEM ) .

用扫描电子显微镜和 透射电子显微镜 分析了碳纤维的结构。

In this retrospective study the researchers compared TEM with TA for both benign and malignant rectal masses .

在这项回溯性分析研究中，研究者比较 TEM与TA，针对良性与恶性直肠肿块进行研究；

Titanate nanotubes were prepared by hydrothermal method and the products were characterized with TEM XRD and XPS .

采用水热法制备了钛酸盐纳米管，并用 TEM、XRD、XPS对其进行了表征。

AFM and TEM results indicated that the nanoparticles after surface modification were monodisperse with coatings on individual nanoparticles .

AFM和 TFM的结果指明，经过表面修饰之后的纳米颗粒是单分散的，每个纳米颗粒均包裹了一层修饰物。

In this paper hot-rolling tests using scanning electron microscopy TEM observation and analysis of EBSD technology microstructure and mechanical properties relationship .

本文通过热轧试验，利用扫描电镜、 TEM观察和EBSD技术等分析显微组织与力学性能之间的关系。

This makes the TEM horn antennas have good fidelity when radiating and receiving short time domain impulse antenna .

TEM喇叭天线作为时域脉冲天线，其辐射和接收的时域短脉冲信号具有良好的保真性。