Using orthogonal design method to develop vinyl chloride-vinyl acetate copolymer paste resin

运用正交设计开发 氯 乙烯- 醋酸 乙烯 酯共聚糊 树脂

A specific emulsifying process was applied to prepare a vinyl acetate / acrylic copolymer modified with epoxy resin which has overcome the disadvantages of vinyl acetate / acrylic emulsion .

采用特殊的乳化工艺使环氧 树脂 与 醋酸 乙烯、丙烯酸单体混溶进行共聚改性，所得的 环氧改性乙丙乳液克服了乙丙乳液的缺点。

The development of vinyl chloride-vinyl acetate copolymer paste resin

氯 乙烯- 醋酸 乙烯 酯共聚糊 树脂的开发

The result shows that vinyl acetate emulsion modified with epoxy resin posseses good stability water resistance and acid resistance .

结果显示， 环氧改性 乙丙乳液有优良的稳定性、耐水性、耐酸性等综合性能。

Preparation of Vinyl Acetate Emulsion Modified with Epoxy Resin

环氧改性 乙丙乳液的研究

Based on vinyl acetate epoxy resin n-butyl acrylate as main monomers and α - Methylacrylic as functional monomer vinyl acetate emulsion modified with epoxy resin by semi-continuous emulsion polymerization is prepared .

采用 醋酸 乙烯 酯、E-44环氧 树脂、丙烯酸丁酯作为主单体，以α-甲基丙烯酸作为官能单体，采用半连续乳液聚合工艺，制备了环氧改性乙丙乳液。