There are a lot of adsorbed oxygen on the surface of unannealed Fe2O3 / SnO2 bilayer and a few adsorbed oxygen left on the surface after annealing .

结果 表明：Fe2O3/SnO2膜表面， 晶格氧的 结合能为 529.85eV，热处理前有大量吸附氧存在，在 600℃退火后，大部分 羟基、 羰基形态的吸附氧 解吸；

XRD structural analysis shows that peak intensity of the annealed sample is greater than that of the unannealed one which demonstrated an increase of crystallinity .

XRD结构分析显示，退火后薄膜样品的峰值强度大于 未 退火样品的强度，说明样品结晶度增强。

On the basis of uniaxial tension test data the Lagrange polynomial interpolation is adopted to construct the stress and strain fields of unannealed and annealed TRBs which can solve the problem of TRB material parameters for simulation .

以单向拉伸试验数据为基础，采用拉格朗日多项式插值法构造了 未 退火和已退火差厚板的应力应变场，解决了数值仿真过程中差厚板的材料参数问题。

However the value of magnetoresistance increased apparently after annealing and was1.74 times the unannealed sample .

而退火后磁电阻值则明显增加，是 未 退火时的1。74倍；

The authors observed the difference from previous experimental results that the resistance to dissolve in Hanks solution for the film deposited by nitrogen ion beam assistance not that annealed film is the best but that unannealed one has been superior to the former .

与已有的实验结果不同，实验中发现，这种N离子束辅助沉积的薄膜在Hanks溶液中的抗溶解特性，不是 退火试样最好而是未退火 状态的膜比前者更优。

The Positron lifetime spectra of unannealed and annealed Ni-coats electro-plated from the four typical baths have been measured .

测量了四种典型镍镀层的采透 火和退火试样的正电子湮没寿命谱。

When the annealed temperature is greater than 600 ℃ the TL peak temperature of the annealed sample is higher than that of the unannealed sample .

陨石样品经 均匀 地 升温退火，退火温度达600℃以上其 诱发TL峰温比 未 经 退火的峰温要高。

The experimental results indicated that the film resistivity of the sample annealed was reduced significantly and only one3.17 of the unannealed .

实验结果表明：退火后样品的薄膜电阻率显著减小，是 未 退火样品薄膜电阻率的 3.17分之一；