The difference of inhibition mechanism of zinc phosphate in aqueous solution and in alkyd coating has been studied by using electrochemical techniques .

应用电化学方法研究了 磷酸 锌在水溶液和醇酸涂层中的缓蚀性能和缓蚀作用机理。

The results of static scale inhibition experiment showed that this series of the multipolymers all have certain inhibition ability to the carbonate zinc phosphate scale and also have good dispersing ability to ferric oxide .

实验结果表明：在海水体系中，该系列多元共聚物对碳酸钙、 磷酸 锌垢均有一定的抑制作用，对氧化铁也有较好的分散作用。

Anti-corrosion property of pigment in studied condition was as follows : organic inhibitor or barium phosphate or zinc oxide > red lead > zinc yellow or zinc phosphate .

在所研究的体系中，防锈颜料的耐蚀性为有机缓蚀剂、磷酸钡、氧化锌＞红丹＞锌格黄、 磷酸 锌。

Preparation of Zinc Phosphate From Low Purity of Zinc Oxide

低纯度氧化锌制备 磷酸 锌研究

Research on process of zinc phosphate

磷酸 锌生产工艺研究

Investigation on Film Formation Mechanism and Performances of Complex Zinc Phosphate Coatings on Magnesium Alloy

镁合金 锌 系复合 磷化膜的成膜机理及性能研究

All-ceramic specimens were luted to the metal alloy by Zinc Phosphate cement glass ionomer cement and composite resin .

将全瓷试件和背景试件分别用树脂粘接剂、玻璃离子粘固粉、 磷酸 锌粘固粉粘接，根据粘接材料的不同分为3组，每组4个。

A new method for the synthesis of lithium zinc phosphate crystals was studied .

对合成 磷酸 锌锂的新方法进行了研究。

This zinc phosphate coating can be treated as pretreatment coating which can improve the adhesion between organic coating and Mg alloy substrate .

该 锌 系 复合 磷化膜作为前处理膜层可提高有机涂层与镁合金基体的附着力。

It was studied the content of pigment and fillers . The results shows that when the proportion between the silicone resin and mica powder aluminum powder zinc phosphate titanium dioxide and kaolin mass is 10:5:2:1:5:2 the coating reached the highest temperature .

实验对颜料、填料用量进行了探讨，结果显示，当有机硅树脂与云母粉、硅酸铝粉、 磷酸 锌、钛白粉、高岭土的质量比例为10：5：2：1：5：2时，涂料的耐高温隔热效果最好。

For the second technics Ammonia / Ammonium Carbonate mixing solvent was used to dissolve low grade Zinc Oxide to produce Zinc ammonium complex which reacted with phosphoric acid to make Zinc Phosphate .

碳铵浸提法采用氨&碳酸铵混合溶剂溶解低品位氧化锌，制得锌氨络合离子，经除杂净化再与磷酸反应制备 磷酸 锌；

Synthesis of Superfine Activated Potassium Zinc Phosphate and It 's Activation Mechanism

活性超细含钾 磷酸 锌的制备及其活化机理的研究

Explored and recorded the curative effect of protecting pulp bottom material glass ion curing agent and self-congealing hl joint zinc phosphate cement posterior teeth with deep caries repaired .

探讨并记录护髓垫底材料玻璃离子粘固剂与自凝氢氧化钙联合 磷酸 锌水门汀治疗后牙深龋的疗效并进行比较。

Study on the Preparation of Zinc Phosphate by Zinc Dross

利用锌浮渣制备 磷酸 锌的研究

A process to prepare aqueous rust-removing and anti-corrosive paint by using polyvinyl acetate emulsion as adhesive phosphoric acid as rust-transforming agent and zinc phosphate and zinc chromate as passivating agent and anticorrosive agent is introduced .

介绍了一种以聚醋酸乙烯酯乳液为基料、以磷酸为锈转化剂、以 磷酸 锌和铬酸锌为钝化剂和防腐剂的水乳型除锈、防锈漆的制备方法。

In order to study the relationship between crystal structure and physical performance of phosphate coating the crystal structure of main components of zinc phosphate coating ( zinc phosphate and ferrous zinc phosphate ) was analyzed .

为研究磷酸盐皮膜结晶结构与其各种物性之间的关系，对 磷酸 锌皮膜主要成分（磷酸锌和磷酸铁锌）的结晶结构进行了分析。

The control group to self-congealing calcium hydroxide cavity lining and zinc phosphate cement basing with curing light compound resin repaired teeth defect .

对照组以自凝氢氧化钙衬洞及 磷酸 锌水门汀垫底后与光固化复合树脂联合修复后牙牙体缺损。

Experimental study on shear bond strength of nano composite zinc phosphate cement for prosthodontics

口腔修复用纳米复合 磷酸 锌水门汀粘接强度的实验研究

The results show that the product is a mixture of zinc phosphate dihydrate and tetrahydrate .

结果表明：产物为二水和四水 磷酸 锌混合物；

All specimens were sealed with zinc phosphate stored in 37 ℃ 100 % humidity .

所有样本均采用 磷酸 锌 水门汀进行封闭，在37℃，100%湿度条件下保存备测。

Phosphorus content in zinc phosphate is determined by phosphorus vanadium molybdate yellow colorimetric method .

采用磷钒钼黄比色法测定 磷酸 锌中磷含量。

The title ultrafine zinc phosphate crystal has been prepared based on zinc nitrate and phosphoric acid as raw materials ammonia as precipitant at the presence of surfactant with an additional crystallization process .

以硝酸锌和磷酸为原料，氨水为沉淀剂，在表面活性剂存在下增加晶化工序，制备了超细 磷酸 锌晶体。

Objective : To develop nano composite zinc phosphate cement .

目的：初步研制纳米复合 磷酸 锌水门汀。

The corrosion behaviors of A3 steel in different pH 3.5 % NaCl modified zinc phosphate and aluminum triphosphate extract solutions have been studied by EIS .

应用EIS研究了A3钢在不同pH值的 磷酸 锌或三聚磷酸铝3.5%NaCl提取液中的腐蚀行为。

Phosphate included : potassium phosphate sodium phosphate aluminum phosphate calcium phosphate iron phosphate zinc phosphate .

磷酸盐包括：磷酸钠、磷酸钾、磷酸铝、磷酸钙、磷酸铁、 磷酸 锌。

Determination of Sulfate in High-purity Zinc Phosphate by Spectroscopic-turbidity Method

分光比浊法测定高纯 磷酸 锌中硫酸根分场对比w_26光度计

Basis of the application of uniform experimental design and the date mining technology the influence of grinding time baking time and baking temperature on the synthesis of lithium zinc phosphate crystals were investigated .

基于均匀设计试验方案以及数据挖掘技术的应用，研究了研磨时间、保温时间、保温温度对 磷酸 锌锂晶体合成的影响。

Roles of zinc phosphate on the corrosion of the scratched epoxy coating

磷酸 锌对环氧涂层破损处金属的缓蚀作用

Zinc phosphate is lamellar crystal with grain diameter of 30 ~ 40nm by XRD and TEM .

该方法制备得到的 磷酸 锌，经XRD和TEM表征为纳米级片状晶体，产品粒径30~40nm。

Synthesis and Characterization of Zinc Phosphate by Hydrothermal Method

水热条件下 磷酸 锌的合成与表征