Zirconium carbide ZrC is an important high temperature structural material with very high melting point excellent strength and good corrosion resistance .

碳化 锆是一种重要的高熔点、高强度和耐腐蚀的高温结构材料。

Zirconium oxychloride with purity of 36.20 % was prepared from zirconium carbide by the process of alkali fusing water washing hydrochloric acid leaching and product crystallization .

以 碳化锆为原料，采用碱熔-水洗-酸浸-结晶工艺制备氧氯化 锆，制得的氧氯化锆产品中ZrO2含量达到36.20%。

Influence of addition of a small amount of Polycarbosilane on the sintering and mechanical properties of zirconium diboride-silicon carbide ceramics

添加少量聚碳硅烷对 ZrB 2-SiC陶瓷烧结和力学性能的影响

The white light and infrared ray absorbing i.e. photothermal conversion properties of Zirconium carbide ( ZrC ) aluminum oxide ( Al 2O 3 ) powder and PP fibers with different ZrC content were measured by IR and dot thermometer and DSC .

采用红外测温仪和点温计等手段测试了 碳化 锆和三氧化二铝的红外线吸收性能，以及含有不同重量的聚丙烯纤维的光热转换性能和热性能。

Preparation of Zirconium Oxychloride via Alkali Fusing of Zirconium Carbide

碳化 锆碱熔制备氧氯化锆的研究