Techniques research of argon arc welding ( A-TIG ) with active agent
带活性 剂的氩弧 焊接（A-TIG）技术工艺研究
In order to improve the spot welding ability of nickel coating the thickness of coating the influence of brighter and wetting agent on the spot welding ability of coating and proposes effective solutions are researched and analyzed .
为了进一步提高镍层的 点焊性，研究、分析了镀层的厚度、镀液中的光亮剂和润湿 剂对镀层点焊性的影响，并提出了有效的解决措施。
This paper expounds the regulations of the influence of the moisture crystallizing mode of weld joint droplet transfer nonmetallic inclusion and other factors in the welding agent of Chrome-Nickel Austenic stainless steel welding rod .
文章阐述了铬镍奥氏体不锈钢焊接焊条 药皮中水分含量、焊缝的结晶模式、熔滴过渡、非金属夹杂因素对 焊缝中气孔的影响规律。
If restoring on the spot well effect can also be obtained when using proper welding process and agent .
若现场修复， 焊接工艺和 选材适宜，也可获得良好的修复效果。
Based on several years of practice experiences of welding crack in cast iron box tire and bearing base including choosing of welding agent and welding process are introduced as well as problems need being focused on in operation .
根据多年的实践，作者介绍了手工电弧焊处理铸铁滚圈、铸铁轴承座开裂问题的一些经验，包括 焊接 材质的选取、焊接工艺的确定以及焊接操作中应注意的问题等。
Welding Agent Reclamation Unit for Automatic Angle Seam Welding Machine for Storage Tank
储罐角缝自动焊机 焊剂回收装置
Welding products as an industrial material joining agent are widely used in various industries .
焊接产品作为一种工业材料连接 剂被广泛地应用于各行各业中。
The paper summarized the characteristics of A-TIG welding process was the composition and usage performance of A-TIG welding activating agent the mechanism of weld reinforcement of A-TIG welding as well as the development and application prospect of welding technology .
A-TIG焊接增加焊缝熔深的机理； A-TIG 焊接技术的发展及应用前景。
A Method for Building a CAPP Integrated System of Welding Components Based on Agent and Feature Technology
融合 智能 体和特征技术的 焊接结构件CAPP集成系统研究
The results show that the bonding strength in the interface hits the record of 95 MPa after the steel core is treated through preheating above the temperature of 400 ℃ and applying surface welding supporting agent of halide solution .
结果表明，表面经机械打磨、酸碱洗并助镀卤化物盐溶液的钢线，在400℃预热复合后，钢线与铜层之间的结合效果较好，界面结合强度达到 95MPa；
Welding agent is a kind of medicament that is used to help welding and improve quality .
焊药是帮助焊接，提高 焊接质量的 药剂。
The result shows that the best welding process is finished by means of flux-cored wire + welding activating agent . After the comparision test on the steel joint it shows the reliability of the examination result the corresponding comments are proposed to the project welding .
结果表明，药芯焊丝加 焊接渗透 剂的工艺方法效果最好，对该钢焊接接头检验方法进行了对比试验，采用PT+RT检验可保证检验结果的可靠性，并对实际工程焊接提出了建议。
焊药