The results show that the stress corrosion is the main failure causing of the bellows expansion joint while the local pit corrosion residual stress and the working stress is the necessary condition .

结果表明，应力腐蚀是该 膨胀 节失效的主要原因，而局部的点蚀和残余应力、工作应力是应力腐蚀的必要条件。

Damage Factors of Bellows Expansion Joint and its Prevention

波纹 膨胀 节失效因素与预防

Study on Corrosion Cracking of Bellows Expansion Joint Made of Stainless Steel

对 真空 制盐 车间不锈钢 膨胀 节热影响 区腐蚀裂纹的探讨

As a result the concerned issues on application of bellows type expansion joint in heat supply network of power plants have been emphasized .

给出了 波纹 管 补偿器对 固定 支架 的 推力计算方法，并指出了在电厂供热管网中使用 波纹 管 补偿器 应注意的问题。

Application of Bellows Expansion Joint in Pressure tested Device of Floating Head Heat Exchanger and Its Analysis Calculation

波形 膨胀 节在浮头式换热器试压装置中的应用及分析计算

Application 0f bellows expansion joint at sintering machine and its ' design considerations

波纹 管 伸缩 节在烧结机中的应用及设计

On the Quality Control of the Manufacturing the U-Form Multilayer Metallic Bellows Expansion Joint

U型多层金属 波纹 管 膨胀 节的制造质量控制

Metal bellows expansion joint is the flexible part used to absorb dimensional changes caused by thermal expansion or contraction or reduce vibration of a pipeline and equipments . It is currently used in various national economy sectors .

金属 波纹 管 膨胀 节作为一种挠性部件，用以补偿因热胀冷缩、机械位移或振动引起的管线、设备等尺寸变化，已广泛用于国民经济的各个部门。

Analysis and Countermeasure of Failure Mechanism of Metallic Bellows Expansion Joint in Piping Line of Blast Furnace Gas

高炉煤气管系用金属 波纹 管 膨胀 节失效机理分析及对策高炉煤气富化技术

Research on the Quotation Method for Bellows Expansion Joint

波形 膨胀 节报价系统研究

Experience of Installation for Metal Bellows - expansion Joint

金属 波纹 管 膨胀 节的安装心得

The establishment of the quality system of the bellows expansion joint .

波纹 管 膨胀 节产品质量体系的建立。

Quality Control of the welding the bellows expansion joint ;

波纹 管 膨胀 节总 成焊接质量的控制；

Computer system of bellows expansion joint design

矩形 烟 风道 波形 补偿器设计计算机系统

Failure Analysis of Bellows Expansion Joint for Blast Furnace Gas

高炉煤气 管线 用 波形 膨胀 节失效分析

Bellows are the basic units of an expansion joint .

波纹 管是组成 膨胀 节的基本元件。

Cracking of bellows expansion joint in FCCU and its prevention

催化裂化装置 膨胀 节的破裂及防止

Both FN 2 and Incoloy steels are most suitable to bellows expansion joint . Using these two steels to replace 18 8 stainless steel can double the service life of bellows expansion joint .

膨胀 节 波纹 管部分采用FN2和Incoloy钢材最好，实践证明，采用上述两种钢材代替188型不锈钢作为制造 波纹管 膨胀 节的材料，可延长膨胀节寿命2倍以上，有很好的经济效益。

Another ambient temperature sensor is the vapor-filled bellows . Selection of Bellows-type Expansion Joint and Bellows Adjustment Device

另一种空气温度传感器是充气 波纹 管。 波纹 管 补偿器与波纹管调长器的选用

Stress assess and analysis for distortion of flue gas turbine inlet bellows expansion joint

烟机入口 膨胀 节变形 过热应力评定及分析

Discussion on Design of the Structural Attachment of Metal Bellows Expansion Joint

金属 波纹 管 膨胀 节某些构件设计问题讨论

Corrosion Failure of Bellows Type Expansion Joint in Heat-supply Pipeline

供热管道 波纹 管 补偿器的腐蚀失效

This paper introduces the experience of installation for metal bellows - expansion joint which is very useful for practical construction .

介绍安装金属 波纹 管 膨胀 节的实际施工经验，它有较大的实用意义。

Development of Bellows Expansion Joint Parametric Drawing Software Based on SolidWorks

基于SolidWorks的 波形 膨胀 节三维参数化绘图软件的开发

Field manufacturing of large-size sub-rigid stainless steel bellows expansion joint in hydropower station

水电站大口径亚刚体不锈钢 波纹 管 伸缩 节的现场制作

This paper presents some information about the design and application of bellows type expansion joint used in heat-supply network taking Yangquan Power Plant No.

以阳泉第二发电厂新建工程为例，介绍了厂区供热管网中 波纹 管 补偿器的设计及应用情况。

This paper proposed overall frame and the realizable method of Bellows Expansion Joint Quotation system .

本文提出了 波形 膨胀 节报价系统的总体框架和实现方法。

Failure analysis and material selection for bellows expansion joint in flue gas expander

烟气轮机管道 膨胀 节的失效原因与选材

The failure analysis on the leaked bellows expansion joint in catalytic cracking unit was investigated .

对某石化公司催化裂化装置中泄漏的大型 波纹 管 膨胀 节进行了失效分析。

The Superplastic Forming Technology of Titanium Alloys Bellows Expansion Joint

钛合金 波形 膨胀 节超塑气胀成形技术研究