The pitting critical potential of the fresh surface is lower than that of the surface covered by passive film . At free-corrosion potential and anodic potential the susceptibility to SCC was very low .

去膜表面发生点蚀的临界电位低于 膜覆盖 表面发生点蚀的临界电位。在自腐蚀 电位和阳极电位条件下，SCC敏感性很低。

C-Si surface melting and α - Si / Si film crystallization are simulated adopting Molecular-dynamics simulation method and S-W potential .

采用S-W 势运用分子动力学方法对硅晶 表面的熔化及α-Si／Si 薄膜的晶化进行了模拟。

After about 30 s the surface of the SS electrode was entirely covered by a thin PANI film where the polymer grew further . Finally the polymerization potential maintained ca. 0.75 V and nano – fibrous PANI film formed .

经历了30s后，电极 表面被一层颗粒状聚苯胺 膜所覆盖，在此基础上，苯胺继续生长，聚合 电位降至0.75V左右并保持稳定，最终形成纳米纤维状聚苯胺。

Cr content had not only a relationship with the structure and thickness of surface oxidizing film but also been largely considered for determining the corrosion potential difference between martix and carbides .

铬元素的含量不仅与 表面 氧化膜的结构和厚度有关，还在很大程度上决定了基体与碳化物的电极 电位差。

Monolayer techniques used for the study of surface film at the air-water interface provide a lot of information of film molecules including optic microscope x-ray wave damping spectroscopy surface potential measurement surface pressure measurement .

对表 面膜的测量研究方法有很多，包括光学显微镜、X射线、波阻尼法、光谱方法、表面膜 电位法、表面膜压法等。