vulcanized latex

硫化橡浆

Examples

  • The effects of the degree of vulcanization on the ionic deposition rate and the physico-mechanical properties of wet-gel and dry-film from vulcanized natural rubber latex were studied .

    本文研究了 硫化 胶乳离子沉积过程，着重探讨了硫化胶乳离子沉积凝胶及胶膜的性能。

  • The contents of elements such as C H N S and so on in the vulcanized latex film from tapping systems A B and C were compared by using of the Element Analyzer .

    用元素分析仪比较了三种割制 硫化 胶乳 胶膜碳（C）、氢（H）、氮（N）和硫（S）元素的含量；

  • The radiation vulcanized latex may be stored for 2 months .

    在2个月内，辐照 硫化 乳液 的 拉伸 强度 基本保持不变。

  • Effects of vulcanizing temperature and time on the physico-mechanical properties of wet-gel and dry-film of vulcanized natural latex were studied .

    本文研究了硫化温度及 硫化时间对凝胶及 胶膜性能的影响，并进一步探索了影响的原因。

  • The development preparation method thermal degradation property and application of natural latex with low protein were related . And the determining method of protein content in low protein latex and the mechanical property of vulcanized latex film with low protein were stated .

    简述了低蛋白天然胶乳的发展、制备方法、热降解性能和应用，并对低蛋白胶乳中蛋白质含量的检测方法和低蛋白 硫化 胶乳 胶膜的力学性能作了 简要的阐述。

  • Influences of certain factors on the properties of vulcanized latex

    一些因素对 硫化 胶乳性质的影响

  • The viscosity of the vulcanized later was higher than that of raw latex but the variation degree of the former latex during storage was lower than that of the latter .

    硫化胶乳的粘度比其生 胶乳大，在贮存过程中的变异幅度比生胶乳小。

  • The results showed that the mechanical properties of vulcanized latex glue membrane of modified NR latex were better when reaction time was 10h and reaction temperature was 35 ?

    结果表明，反应时间为10h，反应温度在35℃时， 所得 胶膜物理机械性能较好；

  • The tensile strength and tear strength of vulcanized reinforced latex film are of 1.3 and 3.45 times of those corresponding properties of control sample respectively and the anti-oxidative and organic solvents resistance behaviors have been increased .

    在气相白炭黑用量13-15份时，补强 胶乳 硫化 胶膜的拉伸强度和撕裂强度分别是对照样品的1.3倍和3.45倍，其耐老化和耐溶剂性能也有较大提高。

  • Studies on vulcanized latex & physico-mechanical properties of ionic deposited WET-GEL and dry-film of vulcanized natural rubber latex

    硫化 胶乳的研究&硫化天然胶乳的离子沉积法凝胶及胶膜的物理性能

  • Vulcanized latex produced from fresh raw latex obviously has a higher viscosity than that of the latex ageing for over three days .

    未陈化的生胶乳制成的 硫化 胶乳，其粘度明显比陈化3天以上制成者高。

  • The standard preparation methods of dried or vulcanized compounded latex films for testing

    非 硫化混合 胶乳膜和干燥混合胶乳 膜的标准制备方法